Should Polymer Clay Be Soft After Baking?

Should polymer clay be flexible after it's been baked? Well the short answer is yes, as long as your bead is under 1cm in thickness. Anything thicker won't be very flexible. Polymer clay is supposed to be flexible if it's baked properly.

How do you know when polymer clay is done baking?

Bake for 15 minutes per quarter inch of thickness. For example, a piece of 1/2" thickness should be cured for 30 minutes. To test the curing, try pressing the tip of your fingernail into the bottom of your piece after it has cooled; it will leave a mark but will not actually enter the clay.

What does polymer clay feel like after baking?

It will break or cut cleanly, without a crumbly texture. Of course the first hint that you're finished baking polymer clay is when your kitchen timer dings. But it won't feel done. Polymer is quite soft when first removed from the oven.